AWG |
Ø Total (mm) |
Ø Desnudo |
Incremento (mm) |
% E |
Regres. (º) |
Abrasión Unidireccional (Gramos-Falla) |
Rigidez. Dielect. (V) |
Rigidez. Dielect. Nylon (V) |
Capa Sencilla |
Capa Doble |
(mm) |
Capa Sencilla |
Capa Doble |
Capa Sencilla |
Capa Doble |
Capa Sencilla |
Capa Doble |
Capa Sencilla |
Capa Doble |
Mín. |
Máx. |
Mín. |
Máx. |
Nom. |
Mín. |
Mín. |
Mín. |
Máx. |
Mín. |
Mín. |
Mín. |
Mín. |
Mín. |
Mín. |
8 |
--- |
--- |
3,315 |
3,383 |
3,264 |
--- |
0,084 |
36 |
--- |
--- |
--- |
--- |
3.300 |
--- |
--- |
9 |
--- |
--- |
2,959 |
3,020 |
2,906 |
--- |
0,081 |
36 |
--- |
--- |
--- |
--- |
3.200 |
--- |
2.875 |
10 |
--- |
--- |
2,642 |
2,695 |
2,588 |
--- |
0,079 |
35 |
--- |
--- |
1.270 |
--- |
6.200 |
--- |
5.575 |
11 |
--- |
--- |
2,357 |
2,408 |
2,304 |
--- |
0,076 |
35 |
--- |
--- |
1.270 |
--- |
6.000 |
--- |
5.400 |
12 |
--- |
--- |
2,106 |
2,151 |
2,052 |
--- |
0,074 |
34 |
--- |
--- |
1.270 |
--- |
5.800 |
--- |
5.225 |
13 |
--- |
--- |
1,882 |
1,923 |
1,829 |
--- |
0,071 |
34 |
--- |
--- |
1.270 |
--- |
5.600 |
--- |
5.050 |
14 |
1,654 |
1,692 |
1,694 |
1,732 |
1,628 |
0,041 |
0,081 |
33 |
42 |
715 |
1.270 |
3.525 |
6.325 |
3.175 |
5.700 |
15 |
1,473 |
1,509 |
1,511 |
1,547 |
1,450 |
0,038 |
0,076 |
33 |
46 |
665 |
1.190 |
3.425 |
6.175 |
3.075 |
5.550 |
16 |
1,314 |
1,349 |
1,352 |
1,384 |
1,290 |
0,036 |
0,074 |
33 |
50 |
625 |
1.115 |
3.325 |
6.000 |
3.000 |
5.400 |
17 |
1,174 |
1,207 |
1,209 |
1,240 |
1,151 |
0,036 |
0,071 |
32 |
54 |
585 |
1.050 |
3.250 |
5.850 |
2.925 |
5.275 |
18 |
1,046 |
1,077 |
1,079 |
1,110 |
1,024 |
0,033 |
0,066 |
32 |
58 |
550 |
980 |
3.175 |
5.700 |
2.850 |
5.125 |
19 |
0,932 |
0,963 |
0,966 |
0,993 |
0,912 |
0,030 |
0,064 |
31 |
62 |
510 |
910 |
3.075 |
5.550 |
2.775 |
5.000 |
20 |
0,835 |
0,861 |
0,863 |
0,893 |
0,813 |
0,030 |
0,058 |
30 |
66 |
475 |
850 |
3.000 |
5.400 |
2.700 |
4.850 |
21 |
0,744 |
0,770 |
0,772 |
0,798 |
0,724 |
0,028 |
0,056 |
30 |
53 |
445 |
800 |
2.925 |
5.250 |
2.625 |
4.725 |
22 |
0,663 |
0,686 |
0,688 |
0,714 |
0,643 |
0,028 |
0,053 |
29 |
58 |
415 |
750 |
2.850 |
5.125 |
2.575 |
4.625 |
23 |
0,594 |
0,617 |
0,620 |
0,643 |
0,574 |
0,025 |
0,051 |
29 |
62 |
390 |
700 |
2.775 |
5.000 |
2.500 |
4.500 |
24 |
0,530 |
0,551 |
0,553 |
0,577 |
0,511 |
0,025 |
0,048 |
28 |
67 |
365 |
655 |
2.700 |
4.850 |
2.425 |
4.375 |
25 |
0,473 |
0,493 |
0,496 |
0,516 |
0,455 |
0,023 |
0,046 |
28 |
72 |
340 |
615 |
2.625 |
4.725 |
2.375 |
4.250 |
26 |
0,422 |
0,439 |
0,442 |
0,462 |
0,404 |
0,023 |
0,043 |
27 |
76 |
325 |
575 |
2.550 |
4.600 |
2.300 |
4.150 |
27 |
0,378 |
0,396 |
0,399 |
0,417 |
0,361 |
0,020 |
0,041 |
27 |
50 |
300 |
540 |
2.500 |
4.500 |
2.250 |
4.050 |
28 |
0,338 |
0,356 |
0,359 |
0,373 |
0,320 |
0,020 |
0,041 |
26 |
55 |
285 |
510 |
2.425 |
4.375 |
2.175 |
3.950 |
29 |
0,302 |
0,320 |
0,322 |
0,338 |
0,287 |
0,018 |
0,038 |
26 |
61 |
265 |
480 |
2.375 |
4.250 |
2.150 |
3.825 |
30 |
0,269 |
0,284 |
0,287 |
0,302 |
0,254 |
0,018 |
0,036 |
25 |
66 |
250 |
450 |
2.300 |
4.150 |
2.075 |
3.725 |
31 |
0,239 |
0,254 |
0,257 |
0,274 |
0,226 |
0,015 |
0,033 |
24 |
--- |
--- |
--- |
--- |
3.825 |
--- |
3.450 |
32 |
0,216 |
0,231 |
0,231 |
0,249 |
0,203 |
0,015 |
0,030 |
24 |
--- |
--- |
--- |
--- |
3,525 |
--- |
3,175 |
33 |
0,191 |
0,206 |
0,206 |
0,224 |
0,180 |
0,013 |
0,028 |
23 |
--- |
--- |
--- |
--- |
3.250 |
--- |
2.925 |
34 |
0,170 |
0,183 |
0,182 |
0,198 |
0,160 |
0,013 |
0,025 |
22 |
--- |
--- |
--- |
--- |
2.975 |
--- |
2.675 |
ESMALTES |
Polivinil Acetal (Formvar) |
Polivinil Acetal (Formvar) + Nylon |
Poliuretano + Nylon |
Poliesterimide + Nylon |
Poliesterimide |
Poliesterimide Soldable + Nylon |
Poliesterimide + Amide Imide |
Clase Térmica |
A = 105 ºC |
A = 105 ºC |
B = 155 ºC |
C = 180 ºC |
C = 180 ºC |
C = 180 ºC |
D = 200 ºC |
Choque Térmico |
a 125 ºC |
a 125 ºC |
a 175 ºC |
a 175 ºC |
a 200 ºC |
a 200 ºC |
a 220 ºC |
Termoplasticidad |
> 180 ºC |
> 180 ºC |
> 170 ºC |
> 200 ºC |
> 300 ºC |
> 200 ºC |
> 300 ºC |
Norma NEMA MW |
15 - C |
17 - C |
28 - C |
24 - C |
30 - C |
78 - C |
35 - C |
Adherencia y Flexibilidad |
El Aislamiento no debe presentar ni grietas ni desprendimiento después del ensayo. |